Enhanced Thin-Film Transistor Performance by Combining 13,6-N-Sulfinylacetamidopentacene with Printed PEDOT:PSS Electrodes

2011

Bottom-contact/bottom-gate organic thin-film transistors (OTFTs) are fabricated using a soluble pentacene precursor (13,6-N-sulfinylacetamidopentacene; SAP) and inkjet printed PEDOT:PSS electrodes on bare SiO2 dielectrics. Saturation mobility, Ion/Ioff ratio, and threshold voltage parameters, respectively, of 0.27 cm2 V−1 s−1, 105, and −4.25 V were measured under ambient conditions after the thermal conversion of SAP to pentacene in 100 μm long channel OTFT devices. The results obtained by the above solution approach are comparable to that of vapor-phase grown pentacene-based OTFTs with photolithographic gold contacts and organic buffer layers and/or inorganic injection layers. The present …

On the Achievement of High performance thin film transistors by employing 13,6-N-sulfinylacetamido pentacene and printed PEDOT:PSS electrodes

2010

SURFACE EFFECTS ON THE GROWTH OF SOLUTION PROCESSED PENTACENE THIN FILMS

2008

13,6-N-Sulfinylacetamidopentacene (SAP) has been transferred on solid substrates both by water-rich environment and organic solvents without altering his chemical structure. Thermal conversion of SAP to pentacene leads to crystals showing similar features of vacuum-sublimated pentacene both in the bulk and thin-film phases. The thin-film phase is strongly affected by the substrate surface properties. Low energy Si-CH3 rich surfaces allow for the formation of compact micrometric crystals following a Volmer-Weber like growth with orientation suitable for field-effect carrier mobility. Screw dislocations along with straight edges are found on these systems as an indication of a loose interlaye…